In accordance with the Copyright Act of 1976, which became effective January 1, 1978, the following statement signed by each author must accompany the manuscript submitted: "I, the undersigned author, transfer all copyright ownership of the manuscript referenced above to the Nigerian Journal of Technological Development, in the event the work is published. I warrant that the article is original, does not infringe upon any copyright or other proprietary right of any third party, is not under consideration by another journal, and has not been published previously. I have reviewed and approve the submitted version of the manuscript and agree to its publication in the Nigerian Journal of Technological Development." A copyright transfer form may be downloaded from the NJTD Website (http://njtd.com.ng/index.php/njtd). Author(s) will be consulted, whenever possible, regarding republication of material. All authors must have access to the data presented and the authors and sponsor (if applicable) must agree to share original data with the editor if requested.
Main Article Content
S.O.A. Olawale
M.A. Kareem
O.Y. Ojo
A.U. Adebanjo
M.O. Thanni
Abstract
The wide variety of industrial and domestic applications of plastic products has fuelled a global trend in their use. The vast amount of plastic items that are discarded after use, on the other hand, pollutes the environment. In light of this, the current study investigated the use of Polyethylene Terephthalate (PET) as substitute for natural sand in concrete production. Locally sourced river sand was replaced with industrially ground waste PET in proportions of 4 to 20% at a step of 4% by the weight of natural sand whereas other concrete constituents (cement, granite, water-cement ratio and superplasticizer) were kept constant. A Grade M40 concrete with a mix proportion of 1:1:2:0.35 (cement: sand: granite: water-to-cement ratio) was used for all concrete mixes. Concrete without PET represents the control. Fresh (Slump) and hardened (compressive, split tensile and flexural) properties of the produced concrete were assessed using standard testing methods. The results showed that the slump of concrete decreased by 1.8% and 12.5% with an increase in PET content from 0 to 20%. The 28-day compressive strength of concrete containing PET was lower than the control. However, concrete with 4% PET compared considerably well with control with the compressive strength value exceeding the target strength of 40 N/mm2 while concretes containing PET beyond 4% had compressive strength below the target strength. The split tensile strength of concrete containing 4% PET was higher than that of the control but exhibited lower flexural strength than the control at the age of 28 days. It was concluded that the reuse of PET as a substitute for natural sand as an alternative waste disposal solution for eco-friendly concrete development and attainment of a pollution-free environment is viable.